PENGARUH DURASI LAS GESEK TERHADAP KEKERASAN DAN KEKUATAN TARIK PADA AS STAINLESS STEEL 304

Khosiq Roviqi, Unung Lesmanah, Artono Raharjo

Abstract


ABSTRACT 

The increasing development of metal-based construction is aligned with the growing use of welding techniques. Friction welding is an innovative welding method used in the industry to join two or more stainless steel materials without using filler metal or melting. As a result, friction welding produces strong and high-quality joints. This study was conducted to determine the effect of varying welding durations on the tensile strength and hardness values of the weld metal and heat-affected zone (HAZ), by varying the welding duration. The welding durations used were 30, 40, and 50 seconds, with a machine rotation speed of 1350 rpm. The material used in this research was 304 stainless steel shaft. The results showed that from the three tests conducted—tensile strength test, weld metal hardness test, and HAZ hardness test—the 50-second welding duration produced the highest values, while the 30-second duration showed the lowest. It can be concluded that the longer the welding duration, the higher the tensile strength, weld metal hardness, and HAZ hardness values.

Keywords: As Stainless Steel 304, Friction Welding, Welding Duration, Tensile Strength, Hardness.

ABSTRAK

Meningkatnya pembangunan kontruksi berbahan logam, selaras dengan peningkatan penggunaan teknik pengelasan. Las gesek merupakan metode pengelasan inovatif yang digunakan dalam industri untuk menggabungkan dua atau lebih bahan logam stainless steel tanpa menggunakan logam pengisi atau leleh, oleh karenanya pengelasan gesek menghasilkan sambungan kuat, dan berkualitas tinggi. Penelitian ini dilakukan bertujuan untuk mengetahui pengaruh variasi durasi pengelasan terhadap kekuatan tarik dan nilai kekerasan weld metal dan HAZ, dengan memvariasikan durasi pengelasan. Durasi pengelasan yang digunakan yakni 30, 40, dan 50 detik, dengan kecepatan putaran mesin 1350 rpm. Penelitian ini menggunakan material As stainless steel 304. Hasil penelitian menunjukkan bahwa dari ketiga pengujian yang dilakukan yakni uji tarik, uji kekerasan weld metal, dan uji kekerasan HAZ, durasi pengelasan 50 detik menunjukkan nilai tertinggi, sedangkan nilai terendah ditunjukkan durasi pengelasan 30 detik. Dapat disimpulkn bahwa semakin lama durasi pengelasan yang dilakukan maka dapat meningkatkan nilai kekuatan tarik, nelai kekerasan weld metal, dan nilai kekerasan HAZ.

 

Kata Kunci: Durasi pengelasan, Las gesek, Kekuatan tarik, Kekerasan, As Stainless Steel 304.


Full Text:

PDF Remote

References


Daftar Pustaka

Chin, W. W. 1998. The Partial Least Squares Aproach to Structural Equation Modeling. Modern Methods for Business Research, 295, 336

Faruq, A., & Rasyid, A. (2020). Pengaruh Sudut Chamfer Male – Female Dan Tekanan Gesek Pada Proses Friction Welding Baja Karbon S45c Terhadap Kekuatan Tarik Dan Struktur Mikro. Jurnal Pendidikan Teknik Mesin Unesa, 1(1), 0–216.

Kurniawan, R., & Yohanes. (2019). Studi Performansi Las Gesek Rotary Pada Penyambunganmildsteeldenganstainless Steel 201. 6, 1–7.

Sumarji. (2011). Studi Perbandingan Ketahanan Korosi Stainless Steel Tipe Ss 304 Dan Ss 201 Menggunakan Metode U-Bend Test Secara Siklik Dengan Variasi Suhu Dan Ph. Jurnal ROTOR, 4(1), 1–8.

Sultoni, N. Finalhalri, & M. AL. Salhbalnal. (2019). ALnallisal Pengalruh Valrialsi Medial Pendingin ALir Daln Oli Paldal Salmbungaln Lalp Joint Terhaldalp Sifalt Mekalnik Menggunalkaln Lals SMALW (DC). Proton, 11(1), 35-42.

Upara, N., & Meindra, A. (2019). Analisis Kekuatan Sambungan Las Gesek Rotary Material Bronze Dengan Stainless Steel Berdasarkan Standard ASME. Seminar Dan Konferensi Nasional IDEC, D14.1-D14.10.


Refbacks

  • There are currently no refbacks.