PENGARUH FRAKSI VOLUME SERAT DAUN NANAS DAN MATRIKS EPOXY TERHADAP KEKUATAN TARIK KOMPOSIT
Abstract
Fibrous composites continue to be developed to become a substitute for metal materials. This is because the nature of the composite material is that it is durable, which are stable, corrosion-resistant, water-resistant, and lightweight compared to metals. Fibers from natural materials are an alternative that can replace synthetic fibers which are more environmentally friendly used as reinforcing fiber for composites. Pineapple leaf fiber is a type of fiber that comes from plants. Pineapple leaves have quite good tensile strength, making them an alternative material for making composites, where pineapple fiber is known for its strength. This research added pineapple leaf fiber to the composite with varying fiber volume fraction percentages of 50%, 60% , 70% and parallel and random orientation. The method used is real experimental using the hand lay-up method. This research created 18 samples divided into 3 samples of each variation, then tested. using ASTM D638-01 standards. This research obtained the highest tensile test results in a parallel orientation with a volume fraction of 70%, a stress value of 102.11 MPa, a strain value of 20.2%, an elastic modulus value of 5.055 MPa. Meanwhile, the random orientation obtained the highest value in the 70% fraction, the stress value was 35.05 MPa, the strain value was 8.7%, the elastic modulus value was 4.028 MPa. This study proved that the addition of pineapple leaf fibers could affect the tensile strength of natural fiber composites.
Â
Keywords: Composite; Pineapple Leaf Fiber; Epoxy Resin; Tensile Test
Â
ABSTRAK
Komposit berserat terus dikembangkan sebagai pengganti material logam. Hal ini dikarenakan sifat material komposit yaitu tahan lama, tahan korosi, tahan air dan lebih ringan dibandingkan logam. Serat alam menjadi alternatif yang menarik bagi serat sintetis yang sering digunakan sebagai serat tekstil dan serat penguat untuk komposit. Pelepah nanas atau (pineapple leaf fibres) serat daun nanas berasal dari jenis (vegetable fibre) atau serat tumbuhan. Serat ini memiliki kekuatan tarik cukup baik, menjadikannya salah satu bahan alternatif untuk membuat material komposit, di mana kekuatannya yang cukup terkenal pada serat nanas ini. Penelitian ini menambahkan serat nanas nanasan  pada komposit dengan variasi persentase fraksi volume serat sebesar 50%, 60% , 70% dan orientasi sejajar dan acak. Metode yang digunakan yaitu eksperimental nyata dengan memakai salah satu metode dari beberapa metode komposit yaitu metode hand lay-up. Penelitian ini membuat 18 sampel terbagi menjadi 3 sampel pada masing-masing variasi, lalu diuji. menggunakan standart ASTM D638-01. Penelitian ini memperoleh hasil uji tarik tertinggi pada orientasi sejajar dengan fraksi volume 70% nilai tegangan sebesar 102,11 MPa, nilai regangan sebesar 20,2%, nilai modulus elastisitas sebesar 5,055 MPa. Sedangkan pada orientasi acak memperoleh nilai tertinggi pada fraksi 70% nilai tegangan sebesar 35,05 MPa, nilai regangan sebesar 8,7%, nilai modulus elastisitas sebesar 4,028 MPa. Penelitian ini membuktikan bahwa kekuatan komposit serat alam khususnya pada uji tarik berpengaruh dengan penambahan serat.
Â
Kata Kunci: Komposit; Serat Daun Nanas; Resin Epoxy; Uji Tarik
References
a. Supriyatna, y. M. Solihin, c. V tri, and u. Jaya, “pengembangan komposit epoxy berpenguat serat nanas untuk aplikasi interior mobil,†2018.
c. Ya’qub1, p. Hartono2, and i. Choirotin3, “analisis serat alam sabut kelapa sebagai bahan material komposit,†2023.
z. Karim, m. Basjir, and c. Yazirin, “pengaruh ketebalan skin komposit sandwich karbon fiber dengan bahan nilon sebagai core terhadap uji bending menggunakan metode vacuum infusion,†2023.
n. Dzaky syamsuri, p. Hartono, and i. Choirotin, “analisis fraksi volume dan orientasi susunan serat kulit batang kersen dan serat pelepah pisang dengan matrik epoxy terhadap sifat mekanik pada komposit,†2023.
s. Habibie et al., “serat alam sebagai bahan komposit ramah lingkungan, suatu kajian pustaka natural fiber as a friendly environmental composite material, a literature review,†2021.
a. D. O. Betené et al., “influence of sampling area and extraction method on the thermal, physical and mechanical properties of cameroonian ananas comosus leaf fibers,†heliyon, vol. 8, no. 8, aug. 2022, doi: 10.1016/j.heliyon.2022.e10127.
m. Yunus et al., “pembuatan dan pengujian sifat mekanik komposit bahan serat fiberglass dan serat daun nanas dengan matrik resin polyester pada panel panjat dinding,†jurnal austenit, vol. 12, no. 1, 2020.
d. N. Susanti, “pengaruh variasi panjang serat nanas terhadap kekuatan tarik dan impact komposit polyester-serat nanas,†2018. [online]. Available: http://repository.unimus.ac.id
supriyanto and jimin, “karakterisik kekuatan komposit serat daun nanas dengan variasi panjang serat,†2021.
s. Sari kelana and f. Choria suci, “dinamika : jurnal ilmiah teknik mesin pengaruh perbandingan fraksi volume serat aren dan serat daun nanas pada pembuatan material komposit,†vol. Xx, no. Y, no. 1, 2021, doi: 10.33772/djitm.v%vi%i.18683.
t. Djunaedi and b. Setiawan, “pengujian kekuatan tarik komposit variasi arah serat roving-resin polyester bqtn r157 yang diproduksi dengan metode vacuum bagging untuk aplikasi pesawat tanpa awak,†2018.
syafrizal, “pengaruh matrik resin-epoxy terhadap kekuatan impak dan sifat fisis komposit serat nanas,†2020.
Refbacks
- There are currently no refbacks.