PENGARUH VARIASI JENIS LARUTAN ANODIZING DAN LAMA WAKTU PADA PROSES SEALING TERHADAP KEKERASAN DAN KETEBALAN LAPISAN HASIL ANODIZING ALUMINIUM ALLOY 1200

Lalu Jefie Reyfaldy, Unung Lesmanah, Ismi Choirotin

Abstract


Abstrak

Pengolahan sumber daya Aluminium murni menjadi sangat penting diketahui serta dipahami demi memenuhi kebutuhan aluminium dalam Masyarakat. Pengolahan aluminium sangat beragam tergantung asal tujuan aluminium tadi akan dijadikan untuk apa nantinya. Salah satu pengolahan aluminium murni yang sudah diketahui ialah anodizing. Anodizing sendiri ialah Teknik pelapisan logam agar terlindungi oleh pengaruh oksidasi. Tujuan dalam dilakukannya anodizing dalam pengolahan bahan logam ialah untuk mendapatkan hasil tampilan logam yang lebih baik serta menarik. Tentunya ada beberapa indikator yang harus dipenuhi dalam keberhasilan proses anodizing. Penelitian ini bertujuan  untuk mengetahui pengaruh variasi jenis larutan asam serta lama waktu proses sealing pada proses anodizing terhadap kekerasan dan ketebalan lapisan pada proses anodizing aluminium alloy 1200.
            Penelitian ini menggunakan metode experiment (experimental research). Data-data dikumpulkan dari hasil pengerjaan benda kerja pada proses anodizing. Proses anodizing dilakukan menggunakan larutan asam sulfat dan asam oksalat, serta menggunakan variasi waktu sealing 10menit, 30menit, & 50menit. Setelah proses anodizing dan sealing pada aluminium alloy 1200, didapatkan data lalu dianalisa menggunakan ANOVA.

 

Abstract

THE EFFECT OF VARIATION OF TYPE OF ANODIZING SOLUTION AND LONG TIME IN THE SEALING PROCESS ON THE HARDNESS AND THICKNESS OF THE 1200 ANODIZING ALUMINUM ALLOY LAYER

The processing of pure Aluminum resources is important to know and understand in order to meet the needs of aluminum in the community. Aluminum processing varies greatly depending on the purpose of what the aluminum is used for later. One of the known processing of pure aluminum is anodizing. Anodizing itself is a metal coating technique to protect it from the effects of oxidation. The purpose of anodizing in metal processing is to get a better and more attractive appearance of the metal. . Of course there are several indicators that must be met in the success of the anodizing process. This study aims to determine the effect of variations in acid solution and length of sealing time in the anodizing process on the hardness and thickness of the coating in the anodizing process of aluminum alloy 1200. This study used an experimental method (experimental research). Data is collected from the results of the workpiece in the anodizing process. The anodizing process was carried out using a solution of sulfuric acid and oxalic acid, and using variations of sealing times of 10 minutes, 30 minutes and 50 minutes. After anodizing and sealing processes on aluminum alloy 1200, data was obtained and analyzed using ANOVA.

 

Keywords : Anodizing, aluminum, sealing time, sulfuric acid, oxalic acid, surface hardness, coating thickness.

Kata Kunci : Anodizing, aluminium, lama waktu sealing, asam sulfat, asam oksalat, kekerasan permukaan, ketebalan lapisan.

Full Text:

PDF Remote

References


S. Harmanto, “Pengaruh Arus Dan Waktu Pelapisan Nikel Dan Tembaga Terhadap Kekerasan Coran Aluminium,” pp. 78–82.

I. Gst Ngr Nitya Santhiarsa, “Pengaruh Kuat Arus Listrik dan Waktu Proses Hard Anodizing pada Aluminium terhadap Kekerasan dan Ketebalan Lapisan,” J. Ilm. Tek. Mesin CakraM, vol. 3, no. 2, pp. 164–169, 2009.

T. P. Raharjo, P. Studi, T. Mesin, F. Teknik, and U. M. Surakarta, “STUDI PENGARUH VARIASI WAKTU PADA PROSES ANODIZING TERHADAP KEKERASAN , KEKASARAN DAN STRUKTUR MIKRO PADA A