OPTIMASI WAKTU DAN TEMPERATUR PROSES ELECTROPLATING BAJA KARBON RENDAH TERHADAP KETAHANAN KOROSI

M. NAFIS YAZDAD

Abstract


The rapid development of science and technology has an impact on the use of metal objects such as jewelry, vehicle parts, and others where the metal has corrosion according to the specifications of the metal. Special treatment is needed to protect the metal from corrosion, one of which is the electroplating process. This study aims to obtain optimal parameters and results according to the specifications of the nickel plating electroplating process against the corrosion rate of low carbon steel ST 41 using the Taguchi optimization method with variations in the electrolyte temperature parameter levels 30oC, 35oC and 40oC. In contrast, the immersion time parameter level variation is 45 minutes, 90 minutes, and 135 minutes. Corrosion rate immersion media using pure seawater for corrosion time of 168 hours, 336 hours, 504 hours, and 720 hours. From the research results, the lowest corrosion rate at 168 hours resulted in a 0.00023 mpy with a weight loss of 0.003 gr. The tremendous corrosion rate at 720 hours resulted in a corrosion rate of 0.00187 mpy with a weight loss of 0.116 gr using the parameter optimal at 40oC electrolyte temperature and immersion time of 135 minutes with a higher SNR value. The higher the electrolyte temperature and the longer the immersion time, the better the coating quantity will be. This is due to an increase in the conductivity of the electrolyte solution and the continuous flow of the ion diffusion rate according to the coating time used

Full Text:

PDF Remote

References


Rasyad Dan B. Budiarto, “Analisis Pengaruh Temperatur, Waktu, Dan Kuat Arus Proses Elektroplating Terhadap Kekuatan Tarik, Kekuatan Tekuk Dan Kekerasan Pada Baja Karbon Rendah,†J. Rekayasa Mesin, Vol. 9, No. 3, Hal. 173–182, 2018, Doi: 10.21776/Ub.Jrm.2018.009.03.4.

M. S. Amin, M. S. Amin, M. Darsin, Dan A. Sanata, “Optimasi

Kekuatan Tarik Proses Electroplating Ss400 Menggunakan Metode Taguchi,†J. Ris. Teknol. Ind., Vol. 14, No. 1, Hal. 54, 2020, Doi: 10.26578/Jrti.V14i1.5839.

Wardana, “Analisis Laju Korosi Baja A36 Dengan Coating Zinc

Anode Dan Aluminium Anode Pada Proses Electroplating,â€

M. Nasution, “Kajian Tentang Hubungan Deret Volta Dan

Korosi Serta Penggunaannya Dalam Kehidupan Sehari-Hari,†Semin. Nas. Tek. Uisu, Vol. 2, No. 4, Hal. 251–254, 2019.

Sumanto Dan R. El Maghfiroh, “Efek Temperatur Terhadap Laju Korosi,†J. Flywheel, Vol. 10, Hal. 26–32, 2019, [Daring].

Tersedia Pada: Https://Ejournal.Itn.Ac.Id/Index. Php/Flywheel/Article/View/722.

W. K. Sabyantoro, H. Purwanto,

Dan M. Dzulfikar, “Analisis LajuKorosi Dengan Aliran Media

Korosi Hcl 10% Pada Material Baja Astm A36 Dengan Sudut Bending,†J. Ilm. Momentum, Vol. 15, No. 1, 2019, Doi: 10.36499/Jim.V15i1.2661.

N. Ngatmin, H. Purwanto, Dan I. Riwayati, “Analisis Laju Korosi Pada Plat Baja Lambung Kapal Dengan Umpan Anoda Korban

Aluminium,†J. Ilm. Momentum, Vol. 15, No. 2, 2019, Doi: 10.36499/Jim.V15i2.3085.

V. M. Pratiwi, Sulistijono, I. P. Hidayat, Dan H. Zuniandra,

“Pengaruh Variasi Waktu Dan Temperatur Kekuatan Lekat Dan

Ketahanan Korosi Pada Baja,†J. Tek. Its, Vol. 8, No. 2, Hal. 218–223, 2019.

D. Sasmita, “Pengaruh Suhu Dan Waktu Pelapisan Tembaga Pada

Baja Karbon Rendah Secara Elektroplating Terhadap Korosi,†mEksakta, Vol. 2, Hal. 61–67, 2016.

D. C. Montgomery, Design And Analysis Of Experiments Eighth Edition. Arizona State University, Vol. 2009, No. 2005. 2013.

Andriawan Dan Aisyah Endah Palupi, “Struktur Mikro , Ketebalan Dan Kekerasan Lapisan Nikel Baja St41,†Jtm, Vol. 07, Hal. 125–134, 2019.

M. B. Nur Rahman, B. Riyanta, Dan D. Agusman, “Pengaruh Temperatur Dan Arus Listrik Proses Pelapisan Krom Pada Plastik Abs Dengan Metode Elektroplating,†Jmpm (Jurnal Mater. Dan Proses Manufaktur), Vol. 4, No. 1, Hal. 58–66, 2020, Doi: 10.18196/Jmpm.4154.

D. R. Setyaningrum, N. Mulyaningsih, C. Pramono, J. T. Mesin, F. Teknik, Dan U. Tidar, “Pengaruh Variasi Waktu Elektroplating Nikel Terhadap Laju Korosi Pada Bejana Penampung Air Nira Lontar Di Industri Nata,†2021.

Muhamad Zainul Efendy Syaefuddin, “Optimasi Parameter Injection Molding Terhadap Shrinkage Pada Material Polypropylene Dengan Metode Taguchi,†Univ. Negeri Malang, 2021.

A. F. Alphanoda, “Terhadap Laju Korosi Pada Hasil PelapisanmElectroplating Hard,†Hal. 286– 291, 2019.

M. Charles Manurung, St., “Pengaruh Kuat Arus Terhadap Ketebalan Lapisan Dan Laju Korosi (Mpy) Hasil Elektroplating Baja Karbon Rendah Dengan Pelapis Nikel,†Visi, Vol. 21, No. 2, Hal. 1857–1869, 2019, [Daring]. Tersedia Pada: Pengaruh Kuat Arus Terhadap Ketebalan Lapisan Dan Laju Korosi (Mpy)%0ahasil Elektroplating Baja Karbon Rendah Dengan Pelapis Nikeacharles Manurung, St.,Mt.

Y. Basjir, Mochammad, “Pengaruh Variasi Waktu Pencelupan Electroplating Nickel – Chrome Pada Baja S45c Terhadap Ketebalan Lapisan,†2021.

D. Nur Robbi, “Pengaruh Variasi Media Pengkarbonan Terhadap Nilai Kekerasan Serta Laju Keausan Baja Assab 7210 Dengan Proses Packcarburizing,†2017.

M. Basjir, “Pengendalian Kualitas Menggunakan Pendekatan Six Sigma Dan Metode New Seventools Sebagai Upaya Perbaikan Produk Defect,†J. Res. Technol., Vol. 21, No. 1, Hal. 1–9, 2020.10

M. Basjir Dan Suhartini, “Analisa Risiko Prioritas Perbaikan Kegagalan Proses Penjernihan Air Dengan Metode Fuzzy Fmea,â€

Tecnoscienza, Vol. 3, Hal. 195–210, 2019.

M. B. Tofani, “Pengaruh Variasi Waktu Pencelupan Plat Baja A36 Terhadap Ketebalan Dan Kekerasan Pelapisan Zn Pada Proses Elektroplating,†Hal. 77–82, 2021.

U. Lesmanah Dan N. Robbi, “Analisa Sifat Mekanis Baja Assab 760 Yang Mengalami Proses Tempering Dengan Variasi Suhu Pemanasan,†J. Tek. Mesin, Hal. 1–5, 2017, [Daring]. Tersedia Pada: Http://Riset.Unisma.Ac.Id/Index.Php/Jts/Article/View/658%0ahttp://Riset.Unisma.Ac.Id/Index.Php/Jts/Article/Viewfile/658/643.


Refbacks

  • There are currently no refbacks.